PURPOSE: A support for regeneration of hard tissue is provided to prevent the outflow of calcium in the initial period of transplant, and to have excellent cellular behavior like high osteanagenesis inductive effect, initial adhesion to cells, propagation, and cytodifferentiation. CONSTITUTION: A manufacturing method of a support for regeneration of hard tissue comprises: a step of synthesizing bioactive glass solution； a step of obtaining bioactive glass by drying and plasticizing the bioactive glass solution； a step of pulverizing the bioactive glass； a step of obtaining paste by mixing the pulverized porous bioactive glass with biodegradable polymers； a step of manufacturing a support from the paste； a step of cleansing and drying the support； a step of coating hydroxyapatite or collagen on the surface of the support； a step of cleansing and drying the coated support； and a step of sterilizing and drying the dried support.본 발명은 다공성생체활성유리를 포함하며 골기질 성분인 하이드록시아파타이트 및/또는 콜라겐이 코팅된 지지체 및 이의 제조방법에 관한 것이다. 상기 지지체의 대략적인 제조과정은 다공성생체활성유리를 제조한 후 생분해성고분자와 혼합하여 지지체를 제조한 후, 상기 전자의 지지체는 생체유사체액에 침지하여 하이드록시아파타이트를 코팅하거나 콜라겐 용액에 침지하여 콜라겐을 코팅하는 방법으로 수행되며, 상기 후자의 지지체는 생체유사체액에 침지하여 하이드록시아파타이트를 코팅한 후 콜라겐 용액에 침지하여 콜라겐을 코팅하는 방법으로 수행된다. 본 발명에서 제조된 다공성생체활성유리를 포함하며 하이드록시아파타이트 및/또는 콜라겐이 코팅된 경조직 재생용 지지체는 인체에 이식한 초기에 과량의 칼슘이 유출되는 것을 막는 효과가 있으며, 높은 골재생 유도효과를 비롯하여 세포에 대하여 초기 접착, 증식 및 분화와 같은 세포의 거동에 있어서 뛰어난 효과를 갖는다.