As a method of manufacturing a medical well-being ceramic ball according to the present invention, based on the total weight of the dough, 20 to 50% by weight of an auxiliary agent containing alumina (Al 2 O 3 ) and carbon, 40 to 60% by weight of loess powder, 10 to 20% by weight of water A kneading step of mixing the% to prepare a dough； Molding the dough into pellets having a spherical shape of 1 to 50 mm； And a drying step of drying the molded pellets at 100 to 120° C. for 24 to 48 hours to complete a well-being ceramic ball. According to the present invention, a well-being ceramic ball containing ocher, that is, a ball-shaped ceramic containing ocher, can be manufactured and used for medical purposes such as applying it to medical devices and tools, thereby maximizing the therapeutic effect, activation of metabolism, and circulation of blood and blood. , Mental and physical stability, insomnia relief, atopy, skin troubles, and shingles, etc. can be treated, which can help the human body.본 발명에 따른 의료용 웰빙 세라믹볼의 제조 방법으로서, 전체 반죽 중량 대비, 알루미나(Al2O3) 및 탄소를 포함하는 보조제 20 내지 50중량%, 황토 분말 40 내지 60중량%, 물 10 내지 20중량%을 혼합하여 반죽을 제조하는, 반죽 단계； 상기 반죽을 1 내지 50mm의 구형의 형상인 펠릿으로 성형하는, 성형 단계； 상기 성형된 펠릿을 100 내지 120℃에서 24 내지 48시간 동안 건조시켜 웰빙 세라믹볼을 완성하는, 건조 단계；를 포함하는 것을 특징으로 한다.본 발명에 따르면 황토를 포함하는 웰빙 세라믹볼, 즉 황토를 포함하는 볼 형상의 세라믹을 제조하여 의료 기기 및 도구에 적용하는 등 의료용으로 사용함으로써 치료 효과를 극대화할 수 있으며 신진 대사의 활성화, 기혈 순환, 심신 안정, 불면증 완화, 아토피와 피부트러블 및 대상포진 등 치료할 수 있어 인체의 건강에 도움을 줄 수 있다.