PROBLEM TO BE SOLVED: To provide composite powder in which zinc oxide particles of which the form is controlled to a rod shape are uniformly treated on the surface of leaf substrate powder by a simple and low cost method which is environmentally friendly, and a cosmetic comprising the composite powder having an excellent use feeling and ultraviolet shield.SOLUTION: Zinc oxide which is controlled to form a rod shape is treated on the surface of leaf substrate powder by using two stages of soft solution reactions. The two stages of soft solution reactions comprise processes I and II. In the process I, a water soluble zinc compound, glycol, an amine compound, metal salt in which one or more kinds of electric charge is +4 or less and leaf substrate powder are mixed to perform the soft solution reaction at 50°C to 100°C. In the process II, the water soluble zinc compound, the amine compound and the powder obtained by the process I are mixed to perform the soft solution reaction at 50°C to 100°C. Consequently, composite powder coated with rod-shaped zinc oxide in which the rod shape has 2 to 200 nm of a minor axis and 50 to 2,000 nm of a major axis, or composite powder calcining the composite powder at 300°C to 1,500°C is obtained. A cosmetic comprises the composite powder.COPYRIGHT: (C)2014,JPO&INPIT【課題】環境に優しく、簡便で低コストな方法にて、形態がロッド状に制御された酸化亜鉛粒子を薄片状基板粉末の表面に均一に処理された複合粉末を提供し、この複合粉末を配合することによって、使用感や紫外線遮蔽に優れた化粧料を提供する。【解決手段】2段階のソフト溶液反応により処理を行うことにより、形態をロッド状に制御された酸化亜鉛を薄片状基板粉末の表面に処理することができる。処理方法は、プロセスIでは水溶性亜鉛化合物とグリコールとアミン化合物および一種または二種以上の電荷が+4以下の金属塩と薄片状基板粉末を混合し、50℃~100℃でソフト溶液反応を行うことにより製造され、プロセスIIにおいて、水溶性亜鉛化合物とアミン化合物とプロセスIにて得られた粉末を混合し、50℃~100℃でソフト溶液反応を行うことにより製造され、短径が2~200nmで長径が50~2000nmのロッド状を形成しているロッド状酸化亜鉛が被覆された複合粉末、又は、該複合粉末を300℃~1500℃で焼成した複合粉末を得る。また、この複合粉末を化粧料に配合する。【選択図】なし