The present invention relates to a method for manufacturing ultrafine particles for increasing absorption capacity of natural egg shell calcium, and more particularly, to a method comprising: a step for washing foreign matters of the egg shell calcium a step for calcining the washed egg shell calcium at 900-1200°C and a step for adding and mixing 321-330 parts by weight of pure water (H_2O) pe 1000 parts by weight of the calcined egg shell calcium. The method for manufacturing ultrafine particles for increasing absorption capacity of natural egg shell calcium according to the present invention simplifies a complicated conventional manufacturing process without using an additional additive or an organic acid, thereby preventing waste of processing chemicals, eliminating a problem of wastewater treatment, shortening manufacturing time and reducing the cost.COPYRIGHT KIPO 2018본 발명은 천연 난각칼슘의 흡수력증대를 위한 초미립자 제조방법에 관한 것으로서, 보다 상세하게는 난각칼슘의 이물질을 세척하는 단계 세척한 난각칼슘을 900℃ ~ 1200℃로 소성하는 단계 소성된 난각칼슘 1000중량부에 대하여 순수(H2O) 321 ~ 330중량부를 첨가 및 혼합하는 단계로 제조하는 것을 특징으로 한다. 본 발명에 따른 천연 난각칼슘의 흡수력증대를 위한 초미립자 제조방법은 별도의 첨가제나 유기산을 사용하지 않고 특히, 종래 복잡한 제조공정을 간단히 하여 처리약품의 낭비방지, 폐수처리문제의 배제효과, 제조시간의 단축 및 비용절감 효과를 달성할 수 있다.