The dental polymerizable composition of the present invention comprises a (meth) acrylic ester polymer (a), a polymerizable monomer (b) containing a (meth) acrylic acid ester and / or (meth) acrylamide, And a polymerization initiator (c). The (meth) acrylate polymer (a) is a homopolymer of (meth) acrylic acid ester and / or a homopolymer having a glass transition temperature of 25 C. to 50 C. The glass transition temperature is higher than 37 C. (Meth) acrylic acid ester and a (meth) acrylic acid ester having a glass transition temperature of homopolymer lower than 37 C., has a glass transition temperature in the range of 25 C. to 50 C., The tan at 37 C. obtained by viscoelasticity measurement is at least 0.10 and does not have melting point.本発明の歯科用重合性組成物は、(メタ)アクリル酸エステル系重合体(a)と、(メタ)アクリル酸エステル及び/又は(メタ)アクリルアミドを含む重合性単量体(b)と、重合開始剤(c)と、を含有する。(メタ)アクリル酸エステル系重合体(a)は、ガラス転移温度が25℃~50℃となる(メタ)アクリル酸エステルのホモポリマー、及び/又は、ホモポリマーのガラス転移温度が37℃より高い(メタ)アクリル酸エステルとホモポリマーのガラス転移温度が37℃より低い(メタ)アクリル酸エステルとのランダム共重合体を含み、25℃~50℃の範囲のガラス転移温度を有し、動的粘弾性測定により求まる37℃におけるtanδが0.10以上であり、融点を有さない。