Disclosed is a mulching film material, comprising the following components in percentage by weight: 5%-30% of micro silicon powder, 1%-10% of starch, 1%-10% of organic silicon, 1%-10% of emulsifier, and the balance of water. The preparation method of the mulching film material comprises: S101, stirring and mixing in proportion the micro silicon powder, starch, organic silicon, emulsifier and water S102, heating the mixed solution, obtained in step S101, at the temperature of 85-100℃ for 5-15 minutes S103, naturally cooling the mixed solution, heated in step S102, to obtain the liquid mulching film material. The mulching film material is simple in formula and low in cost. Due to the simple preparation process, the mulching film material is suitable for large-scale industrial production. The mulching film material is sprayed on the earth surface to form a mulching film, which can insulate heat and retain water, and thus is suitable for crop growth. After being used for a period of time, the mulching film material can be naturally degraded, and thus has little pollution to the environment and soil.Linvention concerne un matériau de film de paillage, comprenant les composants suivants en pourcentages massiques : 5 % à 30 % de micropoudre de silicium, 1 % à 10 % damidon, 1 % à 10 % de silicium organique, 1 % à 10 % démulsifiant, et le reste deau. Le procédé de préparation du matériau de film de paillage comprend les étapes suivantes : S101, agiter et mélanger selon les proportions la micropoudre de silicium, lamidon, le silicium organique, lémulsifiant et leau S102, chauffer la solution mélangée, obtenue dans létape S101, à la température de 85-100 °C pendant 5 à 15 minutes S103, refroidir naturellement la solution mélangée, chauffée dans létape S102, pour obtenir le matériau de film de paillage liquide. Le matériau de film de paillage est de formule simple et de faible coût. Grâce au processus de préparation simple, le matériau de film de paillage est adapté à une pro