PROBLEM TO BE SOLVED: To provide a method for obtaining a collagen membrane, capable of holding sufficient flexibility and elasticity for application to surgery, especially having high tension strength and tear strength.SOLUTION: A production method of a collagen material comprises: a) a step for preparing an acidic natural or modified collagen solution； b) a step for adding an aldehyde crosslinking agent having no reactivity at acidic pH； c) a step for molding or casting the collagen solution； d) a step for processing with ammonia gas, thereby coagulating and crosslinking the collagen solution； e) and a step for removing surplus ammonia, and obtaining the collagen material by drying. The solution used in the step a contains an acidic collagen of 0.05-3 mass%, and coagulation and crosslinking of the collagen solution in the step d) are processed by the ammonia gas, at least 24 hours, preferably.SELECTED DRAWING: None【課題】外科適用のために十分な柔軟性と弾性を保持しつつ、特に、高い引張強さと引裂強さを有するコラーゲン膜を得る方法の提供。【解決手段】ａ）酸型の天然又は変性コラーゲンの水溶液を調製する工程と、ｂ）酸性ｐＨで反応性のないアルデヒド架橋剤を添加する工程と、ｃ）該コラーゲン水溶液を成形又は鋳造する工程と、ｄ）アンモニアガスで処理することによって該コラーゲン水溶液を凝固及び架橋させる工程と、ｅ）余分なアンモニアを除去し、コラーゲン材料を乾燥によって得る工程と、を含む、コラーゲン材料の製造方法。工程ａの水溶液が０．０５～３重量％の酸型コラーゲンを含み、工程ｄ）におけるコラーゲン溶液の凝固及び架橋が、少なくとも２４時間アンモニアガスで処理することが好ましいコラーゲン材料の製造方法。【選択図】なし