According to the present invention, a manufacturing method of a ceramic composition comprises: a step (S210) of weighing and preparing inorganic ingredients comprising 10-12 wt% of macsumsuk, 5-8 wt% of feldspar, 22-25 wt% of iron oxide, 5-10 wt% of Tourmaline, 10-13 wt% of titanium based composite, and 5-8 wt% of mica, and 24-43 wt% of remaining binder ingredients； a step (S220) of obtaining an inorganic mixture by kneading each ingredient obtained in the preparing step and uniformly pulverizing the same with a size ranging from 300 to 400 mesh； a step (S230) of molding the inorganic mixture into a predetermined shape； a primary sintering step (S240) of heating the molded inorganic mixture at a low temperature in a low temperature furnace of 300-600°C for 1-2 hours, and then heating the same in a furnace of 900-1,100°C for 4-5 hours and cooling the same； and a secondary sintering step (S250) of heating the primarily sintered product at a high temperature furnace of 1,500-1,800°C while supplying gases containing nitrogen for 4-6 hours, and gradually cooling the same. The present invention is an inorganic ceramic composition manufactured by the method, and contains functions for relieving stress for a human body or an animal body.본 발명에 의한 세라믹 조성물의 제조방법은 맥섬석 10 ~ 12 중량%와, 장석 5 ~ 8 중량%와, 산화철 22 ~ 25 중량%와, 토르말린 5 ~ 10 중량%와, 티탄계 복합체 10 ~ 13 중량%와, 운모석 5 ~ 8 중량% 로 구성된 무기질 성분과 나머지 바인더 성분 24 ~ 43 중량%를 칭량하여 준비하는 단계(S 210)와, 상기 준비단계에서 얻은 각 성분들을 혼련시키고 300 ~ 400메쉬의 범위로 균질하게 분말화시켜서 무기질 혼합물을 얻는 단계(S 220)와, 상기 무기질 혼합물을 소정의 형상으로 성형하는 단계(S 230)와, 상기 성형화된 무기질 혼합물을 300∼600℃의 저온 소성로에서 약 1∼2시간 동안 저온 가열한 다음, 900 ~ 1100℃의 소성로에서 약 4∼5시간 가열한 다음 냉각하는 1차 소성단계(S 240)와； 상기 1차 소성된 제품을 다시 1500∼1800℃의 고온 소성로에서 질소성분을 함유한 가스를 공급하면서 약 4∼6시간 동안 가열한 다음 서서히 냉각하는 2차 소성단계(S 250)；를 포함하고 있다. 본 발명은 상기 제조방법에 의하여 수득되어지는 무기 세라믹 조성물로서, 인체 또는 동물 신체에 대한 스트레스를 경감시켜주는 기능을 포함하고 있다.