The invention relates to a polymeric bionanocomposite material with antimicrobial and antioxidant properties, intended for medical use, and to a process for preparing the same. According to the invention, the material comprises polylactic acid, epoxidized soybean oil, hydrolysed collagen, vitamin E, compatibilization agent, silver nanoparticles. The process, as claimed by the invention, consists in processing the starting material in melt, at a temperature of 175°C, for 10 min, followed by compression, at a pressure of 200 bar, to result in a material as homogeneous plates with a thickness of 1...4+/-0.05 mm, an elongation of 4.02...39.97 mm, a breaking resistance of 14.88...30.76 MPa, high antimicrobial and antioxidant activity.Invenţia se referă la un material bionanocompozit polimeric, cu proprietăţi antimicrobiene şi antioxidante, pentru uz medical, şi la un procedeu pentru obţinerea acestuia. Materialul conform invenţiei cuprinde acid polilactic, ulei de soia epoxidat, colagen hidrolizat, vitamina E, agent de compatibilizare, nanoparticule de argint. Procedeul conform invenţiei constă în prelucrarea materiilor prime în topitură, la o temperatură de 175°C, timp de 10 min, urmată de o presare la o presiune de 200 bar, din care rezultă un material sub formă de plăci omogene, cu o grosime de 1...4 +/- 0,05 mm, cu o alungire de 4,02...39,97 mm, având o rezistenţă la rupere de 14,88...30,76 MPa, activitate ridicată antimicrobiană şi antioxidantă.