A method for producing a ceramic composition according to the present invention comprises the steps of: mixing 10 to 12% by weight of cristobalite, 5 to 8% by weight of feldspar, 22 to 25% by weight of iron oxide, 5 to 10% by weight of tourmaline, 10 to 13% (S 210) of 24 to 43% by weight of an inorganic component composed of 5 to 8% by weight of mica and the remaining binder component and kneading each of the components obtained in the preparation step to a range of 300 to 400 mesh (S 220) of forming the inorganic mixture into a predetermined shape (S 230), and a step (S 230) of forming the inorganic compound mixture in a low-temperature firing furnace at 300 to 600C A first firing step (S 240) of heating at a low temperature for about 1 to 2 hours, followed by heating at a firing temperature of 900 to 1100C for about 4 to 5 hours, and then cooling And a second firing step (S 250) in which the first fired product is heated again for about 4 to 6 hours while supplying a nitrogen-containing gas in a high-temperature firing furnace at 1500 to 1800C, and then slowly cooled have.The present invention is an inorganic ceramic composition obtained by the above-mentioned production method, and includes a function of alleviating stress on the human body or animal body.본 발명에 의한 세라믹 조성물의 제조방법은 맥섬석 10 ~ 12 중량%와, 장석 5 ~ 8 중량%와, 산화철 22 ~ 25 중량%와, 토르말린 5 ~ 10 중량%와, 티탄계 복합체 10 ~ 13 중량%와, 운모석 5 ~ 8 중량% 로 구성된 무기질 성분과 나머지 바인더 성분 24 ~ 43 중량%를 칭량하여 준비하는 단계(S 210)와, 상기 준비단계에서 얻은 각 성분들을 혼련시키고 300 ~ 400메쉬의 범위로 균질하게 분말화시켜서 무기질 혼합물을 얻는 단계(S 220)와, 상기 무기질 혼합물을 소정의 형상으로 성형하는 단계(S 230)와, 상기 성형화된 무기질 혼합물을 300∼600℃의 저온 소성로에서 약 1∼2시간 동안 저온 가열한 다음, 900 ~ 1100℃의 소성로에서 약 4∼5시간 가열한 다음 냉각하는 1차 소성단계(S 240)와 상기 1차 소성된 제품을 다시 1500∼1800℃의 고온 소성로에서 질소성분을 함유한 가스를 공급하면서 약 4∼6시간 동안 가열한 다음 서서히 냉각하는 2차 소성단계(S 250)를 포함하고 있다. 본 발명은 상기 제조방법에 의하여 수득되어지는 무기 세라믹 조성물로서, 인체 또는 동물 신체에 대한 스트레스를 경감시켜주는 기능을 포함하고 있다.