ZACHODNIOPOMORSKI UNIWERSYTET TECHNOLOGICZNY W SZCZECINIE
发明人:
PAULINA RAGAŃSKA,RAGAŃSKA PAULINA,ADRIAN KRZYSZTOF ANTOSIK,ANTOSIK ADRIAN KRZYSZTOF,ZBIGNIEW CZECH,CZECH ZBIGNIEW
申请号：
PL407149
公开号：
PL225783B1
申请日:
2014.02.12
申请国别(地区):
PL
年份:
2017
代理人:
摘要：
evaluation of adhesion and kohezji coating hardened uv radiation fotoreaktywnych varnish for nail statyczno - dynamic method is characterized by the fact that assessment shall be based on the measured time and load required to destroy the adhesive forces or kohezyjnych la of the clergy isn (2) nail applied between two plates (1, 1 ),and then cured to uv radiation, after which the joined plates (1, 1 ) is unilaterally constant force breaking load (3) one kilogram and every 24 hours another 0.5 kilogram until destruction. if damage occurs at a load of one kilogram and in less than 24 hours is adhesion and kohezj\u0119 is evaluated as niedopuszczaj\u0105ca to apply.if damage occurs during load between 24 and 48 hours and at a load of 1.5 kilograms that adhesion and kohezj\u0119 judged insufficient to use. if damage occurs during load above 48 hours and at load two kilos is adhesion and kohezj\u0119 judged sufficient to apply.if damage occurs during load over 72 hours and at two and a half kilogram load that adhesion and kohezj\u0119 assessed as correct. if damage occurs during load above 96 hours and at load three kilograms this adhesion and kohezj\u0119 is evaluated as good.if damage occurs during load above 120 hours and at the load three and a half kilograms that adhesion and kohezj\u0119 assessed as very good. if damage occurs during load above 144 hours and at a load of four kilograms that adhesion and kohezj\u0119 is estimated as the ideal.Sposób oceny adhezji i kohezji powłok utwardzonych promieniowaniem UV fotoreaktywnych lakierów do paznokci metodą statyczno - dynamiczną charakteryzuje się tym, że oceny dokonuje się na podstawie zmierzonego czasu i obciążenia potrzebnego do zniszczenia sił adhezyjnych lub kohezyjnych lakieru (2) do paznokci, który nanosi się pomiędzy dwie płytki (1, 1), a następnie utwardza się go promieniowaniem UV, po czym połączone płytki (1, 1) obciąża się jednostronnie stałą siłą zrywającą (3) jednego kilograma i dokłada się co 24 godziny