PURPOSE: A method of manufacturing bioceramic pores for bone tissue regeneration and the pores manufactured by the same are provided to have an arranged pore structure with a size bigger than critical dimension required for bone regeneration and to compact a ceramic wall which constitutes bone regeneration. CONSTITUTION: A method of manufacturing bioceramic pores for bone tissue regeneration comprises the following steps: manufacturing ceramic slurry by using bioceramic powder, a binder, a dispersing agent, and a frozen medium； arranging the pores through extrusion molding after freeze molding the ceramic slurry at a freezing point of the frozen medium； primarily heat treating the extruded molding products； and secondarily heat treating the same after removing the frozen medium by freeze drying. The bioceramic powder is selected from a group consisting of hydroxyl apatite, fluoridated hydroxyl apatite, tricalcium phosphate, biphasic calcium phosphate, alumina, zirconia, silica, and bioglass.본 발명은 생체세라믹 분말과 캠핀(camphene)을 캠핀의 융점(예, 60 ℃) 이상의 온도로 가열하여 액상 상태의 균질한 세라믹/동결매체 슬러리를 제조하고, 이를 상온에서 고체화(solidification)시킨 후, 세라믹/캠핀 복합체를 상온에서 압출하여 고체화된 캠핀이 압출 방향으로 고도로 정렬되도록 유도한 후, 이를 세라믹/캠핀 슬러리의 고화온도(solidification point) 근처에서 일정 시간 동안 다시 1차 열처리하여, 캠핀이 압출 방향에 따라 정렬된 방향에 수직한 방향으로만 성장하도록 유도하고, 이를 동결건조하여 제거하고 고온에서 세라믹을 2차 열처리(소결)하여, 골조직 재생에 필요한 임계 크기(예, 100 마이크론) 이상의 정렬된 기공구조를 갖는 고기능성 생체세라믹 다공체의 제조방법 및 이에 의해 제조된 다공체에 관한 것이다.