Magnetic particles have a particle size of 500 nm of less and include a core and a polymer coating that surrounds and encapsulates the core. The core includes a metal, metal alloy, or metal oxide of at least one metal such as B, Mg, Al, Mn, Co, Ni, Cu, Fe Sm, Ln, Yb, Dy, Gd or Er and Nb. The magnetic core is polycrystalline particles which are superspin glass magnetic materials having coercivity greater than zero and magnetic remenance greater than zero at room temperature. Magnetic moment of these superspin glass magnetic materials at low field show increasing with temperature over room temperature. An in situ hydrolysis/precipitation method from precursor metal salts is used to form the polymer-encapsulated magnetic particles.La présente invention porte sur des particules magnétiques (100) qui ont une dimension de particule (134) de 500 nm au maximum et comprennent un cœur (110) et un revêtement polymère (120) qui entoure et encapsule le cœur (110). Le cœur (110) comprend un métal, un alliage métallique ou un oxyde métallique d'au moins un métal tel que B, Mg, Al, Mn, Co, Ni, Cu, Fe Sm, Yb, Dy, Gd ou Er et Nb. Le cœur magnétique (100) est une particule polycristalline et est une matière magnétique de verre à superspin, ayant une coercivité supérieure à zéro et un rémanance magnétique supérieure à zéro à température ambiante. Au-dessus de la température ambiante et à faible champ, le moment magnétique de ces matières magnétiques de verre à superspin augmente avec la température. Un procédé d'hydrolyse/précipitation in situ à partir de sels de métal précurseur est utilisé pour former les particules magnétiques encapsulées par polymère (100).