PROBLEM TO BE SOLVED: To provide a production method of a hard tissue substitute material, by which a coating having hard tissue affinity can be formed by a simple method on a surface of a base body comprising titanium or a titanium alloy, high bonding strength between the base body and apatite can be secured, and furthermore falling of the coating is prevented.SOLUTION: The production method of the hard tissue substitute material includes an alkali treatment step s3, a hot water treatment step s4, and heating treatment step s5. In the alkali treatment step s3, the base body formed of the titanium or the titanium alloy is immersed in an aqueous alkaline solution and the coating containing alkali titanate is formed on the surface of the base body. Then, in the hot water treatment step s4, an immersing operation of immersing the base body on which the coating is formed in hot water at or above 60°C is repeatedly performed for the prescribed number of times. Then, in the heating treatment step s5, the base body after being immersed in the hot water in the hot water treatment step s4 is heated.COPYRIGHT: (C)2013,JPO&INPIT【課題】 チタンまたはチタン合金からなる基体の表面に簡便な方法によって硬組織親和性を有する皮膜を形成することができるとともに、基体とアパタイトとの高い接合強度を確保することができ、さらに、皮膜の脱落が防止された硬組織代替材料の製造方法を提供する。【解決手段】 硬組織代替材料の製造方法は、アルカリ処理工程s3と温水処理工程s4と加熱処理工程s5とを含む。アルカリ処理工程s3では、チタンまたはチタン合金で形成された基体をアルカリ水溶液に浸漬し、基体の表面にアルカリチタン酸塩を含有する皮膜を形成する。次に温水処理工程s4では、皮膜が形成された基体を、60℃以上の温水に浸漬する浸漬操作を、所定の回数繰返し行う。そして加熱処理工程s5では、温水処理工程s4において温水に浸漬した後の基体を加熱する。【選択図】 図2