The present invention provides switchable adhesives comprising a mixture, in proportions by weight, of 20% to 98% of an adhesive, 2% to 80% of curable molecules and 0.05% to 10% of photoinitiator in which the weight proportion of the adhesive is calculated on the basis of its dry weight and wherein the adhesive includes an internal cross-linker for cross-linking the adhesive during drying to provide a cohesive strength in the range 10 to 120 minutes as determined by FINAT test No. 8. Preferably, the adhesive and curable molecules are mutually soluble when dry, or the curable molecules and adhesive may be uniformly dispersed in each other. Preferably the amount of adhesive in the mixture is in the range 40% to 98% by weight, more preferably 60% to 95% by weight, even more preferably 70% to 85% by weight. Preferably the proportion of curable molecules in the mixture ranges from 2% to 60% by weight, more preferably 5% to 40% by weight, even more preferably 15% to 30% by weight. Preferably, the photoinitiator is present in the mixture in the proportions 0.5% to 5% by weight, more preferably 1% to 3% by weight. Such switchable adhesives are useful in medical dressings and other removable sheet products, and may be simply prepared by stirring the adhesive, the curable molecules and the photoinitiator together at room temperature.本発明は重量割合にて２０～９８％のベース接着剤ポリマーの成分と、２～８０％のフリーラジカル重合により硬化可能である硬化性分子と、０．０５～１０％の光開始剤と、を含む混合物を備え、ベース接着剤ポリマーの重量割合は、その乾燥重量に基づいて算出され、かつ、組成物は、FINAT試験法No.18によって計測される５～１００Ｎ／12.7×12.7ｍｍの凝集力とするべく、ベース接着剤ポリマーを乾燥中に架橋させるためにフリーラジカル重合以外の機構により硬化可能な内部架橋剤を含む転換可能接着剤を提供する。好適には、接着剤及び硬化性分子は乾燥状態で相溶であるか硬化性分子と接着剤が互いに均一に分散可能である。好適には混合物中の接着剤が重量にて４０～９８％、より好適には６０～９５％、さらに好適には７０～８５％である。好適には混合物中の硬化性分子が重量にて２～６０％、より好適には５～４０％、さらに好適には１５～３０％である。好適には光開始剤が混合物中に重量にて０．５～５％、より好適には１～３％存在する。この転換可能接着剤は医療用ドレッシング材及び他の除去可能なシート製品に有用であり、接着剤、硬化性分子及び光開始材を室温にて攪拌することにより簡易に調製可能である。