PURPOSE: A salt solid body is a plastically-formed solid salt body that can be used in a building interior material having enough intensity and generates anion which is useful to the body. CONSTITUTION: The baked salt is made by firstly braking the salt at 600~800 temperature degree in 6~8 hours(S1). The anion-emitting salt is made by adding anion-emitting material 1~3 weight per braked slat 100 weight(S3). The mixed salt is made by adding and stirring the phosphate 0.03~0.05 weight per anion-emitting salt 100 weight(S4). The shape of the salt is made by compressing/adding the mixed salt under 1.5~3 pressure in 400~600ton/cm^2(S5). And braking the salt solid body in 600~800°；C for 2~4 hours(S6). After braking, the salt solid body is cooled. Whole or one part of the first braking salt is grinded. The combination salt is made by combining the salt which is not grinded and the grinded salt by weight ratio 20~40:60~80. The first braked salt is grinded into 160mesh and 200mesh. Mixing the 160mesh and 200mesh by weight ratio 3~5:1.본 발명은 음이온을 발생시키는 소금 고형체 및 이의 제조방법에 관한 것으로서, 구체적으로는 음이온을 발생시키도록 소금에 첨가물을 넣고 이를 특정 조건하에서 소성 및 냉각시켜 생성된 소금 고형체 및 그 제조방법에 관한 것이다.구체적으로 본 발명의 소금 고형체는 소금을 600~800℃에서 6~8시간 1차 소성하여 소성소금을 만드는 단계； 상기 소성소금 100중량부당 SiO2 : Al2O3 : TiO2 : MgO의 중량비율이 30~50 : 35~55 : 5~10 : 5~10 포함된 음이온 발생물질을 1~3중량부 첨가하여 음이온발생소금을 만드는 단계； 상기 음이온발생소금 100중량부당 인산마그네슘 0.03~0.05중량부를 첨가하고 교반하여 혼합소금을 만드는 단계； 상기 혼합소금을 1.5~3기압 하에서 400~600ton/㎠로 가압·성형하여 소금 고형체의 형상을 만드는 단계； 상기 소금고형체를 600~800℃에서 2~4시간 2차 소성하는 단계； 상기 2차 소성 후, 상기 소금 고형체를 냉각하는 단계를 거쳐 제작되는 것을 특징으로 한다.