The invention relates to a process for preparing a reticulated structure for biomedical application. According to the invention, the process comprises the synthesis of the copolymer based on itaconic anhydride and 3,9-divinyl-2,4,8,10-tetra-oxaspiro[5,5]undecan, by a copolymerization reaction in 1,4-dioxane solution, at molar ratios of 1:0.5 and 1:2 with radical initiator 2,2-azobis(isobutyronitrile) added in three stages, at a temperature of 75°C, for 17 h, while stirring at 250 rpm, to result in a copolymer in solution to be precipitated in anhydrous diethyl ether, separated and dried at 30°C, after which it is admixed, in a 1,4-dioxane solution having a concentration of 20%, with hyaluronic acid in a concentration of 1% in water, at the ambient temperature of 22°C, for 24 h, in stationary regime, subjected to dialysis and lyophilization, finally resulting in a gel structure with double sensitive character: to temperature and pH.Invenţia se referă la un procedeu de obţinere a unei structuri reticulate cu aplicaţii biomedicale. Procedeul conform invenţiei constă în sinteza, printr-o reacţie de copolimerizare în soluţie de 1,4-dioxan, a copolimerului pe bază de anhidridă itaconică şi 3,9-divinil-2,4,8,10-tetra-oxaspiro[5.5]undecan, în rapoarte molare 1:0,5 şi 1:2, cu iniţiator radicalic 2,2-azobis(izobutironitril) adăugat în trei trepte, la temperatura de 75°C, timp de 17 h, sub agitare de 250 rot/min, rezultând copolimerul în soluţie care se precipită în dietileter anhidru, se separă şi se usucă la temperatura de 30°C, după care se amestecă în soluţie de concentraţie 20% în 1,4-dioxan cu acid hialuronic de concentraţie 1% în apă, la temperatura de 22°C a mediului, timp de 24 h, în regim staţionar, dializare şi liofilizare, rezultând o structură de gel având caracter dublu senzitiv: cu temperatură şi pH.