A method for producing a foam foam for supporting a liquid cosmetic material capable of supporting and using a liquid or solid cosmetic composition such as a solution, emulsion, gel, cream or suspension, After putting it in a chamber, withdrawing air at a temperature of 55 to 65 C., sedating for 60 minutes under 0.1 to 0.2 KPa atmospheric pressure condition, after lowering the temperature to 25 to 35 C., nitrogen is supplied and 2 to 3 KPa (B) putting the polyether polyol into a chamber, sedating for 60 minutes at a temperature of 15 to 25 C and a pressure of 0.1 to 0.2 KPa under atmospheric pressure conditions, Supplying nitrogen, sedating for 48 hours under atmospheric pressure conditions of 2 to 3 KPa to prepare a polyether polyol, (c) a step of preparing a foaming agent, a catalyst agent and (D) a polyester polyol, a polyether polyol, a foaming agent, a catalyst agent and a surfactant are sequentially introduced into a mixing and stirring tank according to a mixing ratio, Continuous foaming while stirring at 5,000 rpm per minute under conditions of a temperature of 22 to 24 C. and a tank internal pressure of 3 KPa (e) a step of aging the foamed foam to be formed for 48 hours after completion of the foaming step , And (f) cutting the foamed foam into a product to produce a foamed foam for carrying a liquid cosmetic material.Selection drawing None溶液、エマルジョン、ゲル、クリームまたは懸濁液など、液状または固状の化粧料組成物を担持して使用することができる液状化粧料担持用発泡フォームの製造方法に係り、(a)ポリエステルポリオールをチャンバに入れ、温度55~65℃、空気を抜き取り、0.1~0.2KPa気圧条件で60分間鎮静にした後、温度を25~35℃に下げた後、窒素を供給し、2~3KPa気圧条件で48時間鎮静にし、ポリエステルポリオールを準備する段階と、(b)ポリエーテルポリオールをチャンバに入れ、温度15~25℃、0.1~0.2KPa気圧条件で60分間鎮静にした後、窒素を供給し、2~3KPa気圧条件で48時間鎮静にし、ポリエーテルポリオールを準備する段階と、(c)容量の需要に応じて、発泡剤、触媒剤及び界面活性剤をそれぞれタンクに注入して準備する段階と、(d)ポリエステルポリオール、ポリエーテルポリオール、発泡剤、触媒剤及び界面活性剤を、配合比率によって、混合撹拌タンクに順次に投入した後、温度22~24℃、タンク内部圧力3KPaの条件で、分当たり5,000rpmで撹拌しながら連続発泡させる段階と、(e)発泡段階が完了した後、形成される発泡フォームを48時間熟成させる段階と、(f)発泡フォームを裁断して製品化する段階と、を含んでなる液状化粧料担持用発泡フォームの製造方法である。【選択図】なし