In a process of fabricating a stent composed primarily of niobium alloyed with a trace amount of zirconium, tantalum, or titanium for hardening, the stent is annealed under vacuum in a substantially oxygen-free environment. The vacuum is preferably maintained at pressure less than 10-4 millibars, oxygen-content less than about 80 parts per million, and the annealing temperature exceeds 400°C for at least one hour, and is preferably kept in a range from about 1100-1200°C for several hours. This may be followed by applying a surface layer of oxide, such as iridium oxide, with a thickness of 299-300 nm to the stent.Linvention concerne un procédé de fabrication dun stent essentiellement constitué de niobium allié à des traces de zircon, de tantale ou de titane à des fins de durcissement, ledit stent étant recuit sous vide dans un environnement essentiellement libre doxygène. Le vide est de préférence maintenu à une pression inférieure à 10-4 millibars, la teneur en oxygène est inférieure à 80 parties par million, et la température de recuit est supérieure à 400 °C sur au moins une heure et est maintenue à 1100-1200 °C sur plusieurs heures. La phase de recuit peut être suivie par lapplication dune couche de surface doxyde, tel quoxyde diridium, avec une épaisseur de 299-300 nm, sur le stent.