process to obtain a composite magnetic coatings for systems in medicine odtw\u00f3rczej is that magnetic powder of uziarnieniu from 100 to 200 mm shall be subjected to digestion 5% citric acid or 5% oxalic acid for 3 to 5 minutes in a temperature 20\u00b0c.then to 97% by weight is added to the magnetic powder 3% by weight methyl polimetakrylanu powders densified liquid monomer in the form of methylmethacrylate, and the resulting mixture is homogenised with the weight ratio of the polymer in the form of powder to liquid monomer is about d 1: 1 to 3: 1, which is placed in the input form and subjected to pressing under pressure from 20 to 50 bars,and wyprask\u0119 polimeryzuje in water bath at a temperature of 20\u00b0c to 90\u00b0c in time from 3 to 20 minutes. in turn utwardzon\u0105 wyprask\u0119 subjected magnesowaniu.Sposób otrzymywania kompozytu magnetycznego dla układów retencyjnych w medycynie odtwórczej polega na tym, że proszek magnetyczny o uziarnieniu od 100 do 200 µm poddaje się trawieniu 5% kwasem cytrynowym albo 5% kwasem szczawiowym przez 3 do 5 minut w temperaturze 20°C. Następnie do 97% wagowych proszku magnetycznego dodaje się 3% wagowe polimetakrylanu metylu w postaci proszku utwardzonego płynnym monomerem w postaci metylometakrylanu, a uzyskaną mieszaninę homogenizuje się, przy czym stosunek wagowy polimeru w postaci proszku do płynnego monomeru wynosi od 1:1 do 3:1, uzyskany wsad umieszcza się w formie i poddaje prasowaniu pod ciśnieniem od 20 do 50 barów, a wypraskę polimeryzuje się w kąpieli wodnej w temperaturze od 20°C do 90°C w czasie od 3 do 20 minut. Z kolei utwardzoną wypraskę poddaje się magnesowaniu.