The present invention relates to a Dissolving the bioresorbable polyester in a first solvent to form a polymer solution； b. Contacting the polymer solution with a second solvent which is a non-solvent and predominantly water for the bioresorbable polyester to precipitate the bioresorbable polyester in the form of a wet polymeric material； c. Pre-drying the wet polymeric material at a temperature below the TgO of the bioresorbable polyester, d. Pulverizing the pre-dried polymer material into polymer particles having a size of less than 10 mm, e. The pulverized polymer particles comprising 1% dry residue content of less than w / w in less than TgO of the biological material absorbent polyester, f. The polymer particles from step e of the biological material absorbent polyester gOT to TgE Post-treating at a temperature in the range, and g. A bulk density of greater than or equal to 0.3 g / ml, greater than or equal to 0.4 g / ml, comprising grinding the polymer particles from step f) into a powder having a d 50 of from 1 to 300 μm and a particle size of d 90 of greater than 30 to up to 3000 μm Or more and a specific surface area of 2.0 m <； 2 >； / g or less. The present invention also relates to a method for producing a bioresorbable polyester powder in powder form.본 발명은 a. 생체재흡수성 폴리에스테르를 제1 용매 중에 용해시켜서 중합체 용액을 형성하는 단계, b. 중합체 용액을, 생체재흡수성 폴리에스테르에 대해 비-용매이며 주로 물인 제2 용매와 접촉시켜서 생체재흡수성 폴리에스테르를 습윤 중합체 물질의 형태로 침전시키는 단계, c. 습윤 중합체 물질을 생체재흡수성 폴리에스테르의 TgO 미만의 온도에서 사전 건조시키는 단계, d. 사전 건조된 중합체 물질을 10 mm 미만의 크기를 갖는 중합체 입자로 분쇄하는 단계, e. 분쇄된 중합체 입자를 생체재흡수성 폴리에스테르의 TgO 미만에서 1% 중량/중량 이하의 잔류 물 함량으로 건조시키는 단계, f. 단계 e로부터의 중합체 입자를 생체재흡수성 폴리에스테르의 TgO 내지 TgE범위의 온도에서 후처리하는 단계, 및 g. 단계 f로부터의 중합체 입자를 1 내지 300 μm의 d50 및 30 초과 내지 최대 3000 μm의 d90의 입자 크기를 갖는 분말로 분쇄하는 단계를 포함하는, 0.3 g/ml 이상의 벌크 밀도, 0.4 g/ml 이상의 탭 밀도 및 2.0 m2/g 이하의 비표면적을 갖는 분말 형태의 생체재흡수성 폴리에스테르를 제조하는 방법에 관한 것이다.