The invention relates to a process for preparing a material with regenerative properties, used as bone substitute material in the orthopedic and oral and maxillofacial surgery. The claimed material is prepared by carrying out, in a first step, a porous ceramic structure of &bgr -TCP, by precipitating in distilled water solutions of 30% concentration of ammonium hydrogen phosphate and calcium nitrate tetrahydrate at 38°C, for 60 min, while stirring at 800 rpm, at a controlled pH of 8...8.5, filtering, washing and drying for 12 h in a cabinet dryer, followed by calcining at 800°C for 2 h and preparing a ceramic suspension with a solid content of 75% by homogenization with sodium polyacrylate and polyethylene oxide, impregnating a polyurethane foam, drying, sintering and sterilizing the resulting porous ceramic structure, then, in a second step, the ceramic structure is screened on sieves with meshes of 45...125 &mum, 125...250 &mum, 500...1000 &mum and 1000...2000 &mum, there resulting a reproducible material of resorbable &bgr -TCP as four size-types, with apparent densities within the range of 1.186...0.7905 g/cm.Invenţia se referă la un procedeu obţinere a unui material cu proprietăţi regenerative, utilizat ca material de substituţie osoasă în chirurgia ortopedică şi oro-maxilo-facială. Materialul conform invenţiei se obţine prin realizarea, într-o primă etapă, a structurii ceramice poroase din β -TCP, prin precipitarea din soluţii, în apă distilată, cu concentraţii de 30% de fosfat acid de amoniu şi azotat de calciu tetrahidrat, la 38°C, timp de 60 min, sub agitare la 800 rpm, la unH controlat la 8...8,5, filtrarea, spălarea şi uscarea timp de 12 h la etuvă, urmată de calcinarea la 800°C, timp de 2 h, şi prepararea unei suspensii ceramice cu 75% solid, prin omogenizare cu poliacrilat de sodiu şi oxid de polietilenă, impregnarea unei spume polimerice, uscarea, sinterizarea şi sterilizareastructurii ceramice poroase rezultate, după care, într-o a doua etapă, se