A preparation method for a medical porous metal implant material comprising mixing tantalum powder, a pore-forming agent, and a forming agent into a powder mixture, then granulating, injecting into a mold for forming, demolding, degreasing, sintering, and performing a heating process to produce the medical porous metal implant material for dental bone tissue replacement the pore-forming agent is one or multiple of sodium bicarbonate, urea, sodium chloride, methyl cellulose, and ethyl cellulose, and the forming agent is one or multiple of polyvinyl alcohol, stearic acid, zinc stearate, paraffin, and synthetic rubber the degreasing process comprises: gradually increasing the temperature to 400 to 800°C at a speed of 0.5 to 3°C/min, introducing argon gas to form a protective atmosphere, and maintaining the temperature for 60 to 240 minutes Effective improvements to the sintering and heating process steps substantially enhance the mechanic properties of the produced porous tantalum material, thereby enabling the material to be very suitable as a medical implant material for human dental bone tissue replacement.Procédé de préparation dun matériau métallique poreux à usage médical, selon lequel la poudre de tantale est mélangée à un agent de formation de pores et un agent moulant pour obtenir une poudre synthétique granulée, qui sera ensuite injectée dans le moule en vue de son moulage, démoulée, frittée et traitée thermiquement de manière à obtenir un matériau métallique poreux de substitution de tissu osseux dentaire pour implant médical. Lagent de formation de pores représente un ou plusieurs parmi bicarbonate de sodium, urée, chlorure de sodium, métyhlcellulose, éthylcellulose et lagent moulant est un ou plusieurs parmi alcool polyvinylique, acide stéarique, stéarate de zinc, paraffine et caoutchouc synthétique. Létape de décrassage seffectue à une vitesse de 0,5 à 3° C/min afin datteindre entre 400 et 800° C de telle sorte que largon forme une atmosphère protectrice