The present invention discloses a method of making a bearing component of a medical implant suitable for use as an artificial joint, the method comprising: - preheating a crosslinked polymeric bulk material to a temperature 80°C and below the melting point of the polymeric material, wherein the bulk material is characterized by having an axial direction and a transverse direction orthogonal to the axial direction and is further characterized by a dimension d1 in the transverse direction； - applying deforming pressure to the bulk material to change the dimension from d1 to d2, where d2 is less than d1； and - machining the bearing component from the extruded bulk material, wherein the load bearing axis of the bearing component corresponds to the axial direction of the crosslinked bulk material. Preferably, the crosslinked polymeric bulk material is crosslinked ultra high molecular weight polyethylene (UHMWPE).Cette invention concerne le traitement, par déformation à l'état solide, de polymères réticulés de poids moléculaire élevé, tels que le PEUHPM (UHMWPE). Par exemple, une extrusion en dessous de la transition de fusion produit des matériaux qui combinent une résistance à la traction et une stabilité à l'oxydation élevées. Les matériaux sont particulièrement appropriés pour servir de composants de roulement dans les hanches artificielles et autres implants. Les matériaux en vrac traités sont anisotropes et ont une solidité plus élevée dans le sens axial. Le matériau est stable à l'oxydation même après quatre semaines de vieillissement accéléré dans un récipient sous pression contenant cinq atmosphères d'oxygène (ASTM F2003). En raison de sa stabilité à l'oxydation, le matériau traité par déformation est un candidat approprié pour les emballages perméables à l'air et la stérilisation gazeuse, jusque-là réservée au PEUHPM (UHMWPE) réticulé refondu.