The invention relates to a process for preparing a nanogel for biomedical applications. According to the invention, the process consists in that a 20% solution of poly(itaconic anhydride-co-3,9-divinyl-2,4,8,10-tetra-oxaspiro [5.5]undecane) copolymer in dioxane is mixed with a 0.5% solution of riboflavin in dimethyl sulphoxide, in a gravimetric ratio of 0.6/0.015, at a temperature of 40°C, maintained for 120 min at daylight or in the presence of UV radiation for gradual formation of nanogel particles, followed by precipitating the same in diethyl ether, separating by centrifugation, then precipitating twice in diethyl ether for removing unreacted compounds and drying in vacuum oven at 25°C, at a pressure of 600 mmHg, for 24 h.Invenţia se referă la un procedeu de obţinere a unui nanogel pentru aplicaţii biomedicale. Procedeul, conform invenţiei, constă în aceea că se amestecă o soluţie 20% de copolimer poli(anhidridă itaconică-co-3,9-divinil-2,4,8,10-tetra-oxaspiro[5.5]undecan) în dioxan cu o soluţie 0,5% riboflavină în dimetilsulfoxid, în raport gravimetric 0,6/0,015, la temperatura de 40°C, cu menţinere timp de 120 min la lumina zilei sau în prezenţa radiaţiei UV pentru formarea treptată a particulelor de nanogel, se precipită în dietil eter, se separă prin centrifugare, după care se precipită de două ori în dietil eter pentru îndepărtarea compuşilor nereacţionaţi şi se usucă în etuva de vid la 25°C şi presiunea de 600 mmHg, timp de 24 h.