The purpose of the notification is to obtain polymer layers on the surface of titanium or titanium alloys on a polymer basis with phosphates and medicinal products characterised by the fact that titanium or titanium alloy oxidises anode in a water bath containing calcium phosphorus of the concentration 0001 mol/dm3 -10 mol/dm3 using a compression voltage in range from 0,1 V to 800 V, the anode current density of 5 -500 A/dm2 and subsequently the oxidised titanium or titanium alloy is placed in a solution based on adipic acid, a solvent that is favourable to dichloromethane,an antibiotic or a non-steroidal anti-inflammatory drug or an immunosuppressant or an antifungal or antiviral medicine used in the treatment of hard circulating tissues, in quantities of 0, 0001 g/L to 1000 g/L and insoluble zinc phosphate positive (Zn3(PO4)2) and/or phosphate positive copper (Cu3(PO4)2) and/or silver phosphate positive (Ag3PO4),and then it dries.Przedmiotem zgłoszenia jest sposób otrzymywania warstw polimerowych na powierzchni tytanu lub stopów tytanu na bazie polimeru z fosforanami i lekami charakteryzujący się tym, że tytan lub stop tytanu utlenia się anodowo w kąpieli wodnej zawierającej podfosforyn wapnia o stężeniu 0,001 mol/dm3 - 10 mol/dm3 stosując napięcie zaciskowe w zakresie od 0,1 V do 800 V, anodową gęstością prądu w zakresie 5 - 500 A/dm2 a następnie tak utleniony tytan lub stop tytanu umieszcza się w roztworze na bazie pochodnej kwasu adypinowego, rozpuszczalnika korzystnie dichlorometanu, leku korzystnie antybiotyku lub leku przeciwzapalnego korzystnie niesteroidowego lub leku immunosupresyjnego lub leku przeciwgrzybicznego lub leku przeciwwirusowego stosowanego w leczeniu tkanek twardych okołowszczepowych, w ilości od 0,0001 g/L do 1000 g/L oraz nierozpuszczalnych związków fosforanów cynku korzystnie (Zn3(PO4)2) i/lub fosforanów korzystnie miedzi korzystnie (Cu3(PO4)2) i/lub fosforanów srebra korzystnie (Ag3PO4), a następnie suszy.