The purpose of the notification is to produce a polylactide substitute for the hydrophilic sponge bone in which a solution of polylactide in dioxin concentration 1 -12%is produced,to this solution is added a copolymer of methacrylic acid in the quantities of 0,01 -100% by weight compared to polylactide, followed by porophorus, selected from water and alcohol of C1 -C3, in the quantities of 0,1 -30% by volume compared to the solution of polymer, mixed by 3-24 h at 20-60-C temperature at 160-300 rpm, after which the solution is poured into the form and frozen at the temperature -25- -35-oC, by 12-36-h, the resulting substitute is left in the water, at the temperature -10-C-10-oC to 3-5 days, then vacuum-dried at the temperature 30-45oC to 24-48-h.Przedmiotem zgłoszenia jest sposób wytwarzania polilaktydowego substytutu kości gąbczastej o zwiększonej hydrofilowości, w którym sporządza się roztwór polilaktydu w dioksanie o stężeniu 1 - 12%, do tego roztworu dodaje się kopolimer kwasu metakrylowego w ilości 0,01 - 100% masowych w stosunku do polilaktydu, po czym dodaje się porofor, wybrany spośród wody i alkoholu C1 - C3, w ilości 0,1 - 30% objętościowych w stosunku do roztworu polimeru, mieszaninę miesza się przez 3 - 24 h w temperaturze 20 - 60°C, z szybkością 160 - 300 rpm, po czym roztwór wylewa się do formy i zmraża się w temperaturze -25- -35°C, przez 12 - 36 h, następnie otrzymany substytut pozostawia się w wodzie, o temperaturze -10°C- 10°C na 3 - 5 dni, po czym suszy się próżniowo w temperaturze 30 - 45°C przez 24 - 48 h.