The invention relates to a method for the thermomechanical treatment of a titanium alloy comprising between 23 and 27% niobium by atomic proportion, between 0 and 10% zirconium, and between 0 et 1% oxygen, nitrogen and/or silicon, wherein the following steps are carried out: a) an increase in the temperature of the sample of the alloy to a temperature above 900°C b) a rapid quenching c) a severe cold deformation and d) an aging treatment at a temperature between 200 and 600°C, the duration of the treatment being between 10 seconds and 10 minutes. The invention further relates to an alloy obtained by said method and to prostheses produced from such an alloy.Procédé de traitement thermomécanique dun alliage de titane, alliage et prothèse ainsi obtenus. Selon un procédé de traitement thermomécanique dun alliage de titane comportant entre 23 et 27% de niobium en proportion atomique, entre 0 et 10% de zirconium, et entre 0 et 1% doxygène, dazote et/ou de silicium, on procède aux étapes suivantes: a) une montée dun échantillon de lalliage à une température supérieure à 900°C b) une trempe rapide c) une déformation à froid sévère d) un traitement de vieillissement à une température comprise entre 200 et 600°C, la durée du traitement de vieillissement étant comprise entre 10 secondes et 10 minutes. Alliage obtenu par ce procédé et prothèses réalisées dans un tel alliage.