The invention relates to a kit of parts for preparing a glass ionomer cement, the kit comprising a Part A and a Part B, Part A being a powder and comprising an acid-reactive filler in an amount above about 60 wt. %, the acid-reactive filler having a mean particle size in the range of 3.5 to 10 μm, an non acid-reactive filler in an amount above about 1 wt. %, the non acid-reactive filler having a mean particle size in the range of 1.0 to 3.5 μm, Part A not comprising a polyacid in an amount above about 1 wt. %, wt. % with respect to the weight of Part A, Part B being a liquid and comprising a polyacid in an amount above about 30 wt. %, water, a complexing agent, wt. % with respect to the weight of Part B. The invention also relates to a process of producing a hardenable or hardening composition and use thereof in the dental field.L'invention concerne un kit de parties de préparation d'un ciment de verre ionomère, le kit comprenant une Partie A et une Partie B, la Partie A étant une poudre et comprenant une charge réactive à l'acide dans une quantité supérieure à environ 60 % en poids, la charge réactive à l'acide ayant une taille de particule moyenne dans la plage de 3,5 à 10 µm, une charge non réactive à l'acide dans une quantité supérieure à environ 1 % en poids, la charge non réactive à l'acide ayant une taille de particule moyenne dans la plage de 1,0 à 3,5 µm, la Partie A ne comprenant pas un polyacide dans une quantité supérieure à environ 1 % en poids, % en poids par rapport au poids de la Partie A, la Partie B étant un liquide et comprenant un polyacide dans une quantité supérieure à environ 30 % en poids, de l'eau, un agent complexant, % en poids par rapport au poids de la Partie B. L'invention concerne également un procédé de production d'une composition durcissable ou durcissante ainsi que son utilisation dans le domaine dentaire.