The present invention relates to a method for producing artificial reefs using porous foam stone, Preparing a basic material by mixing 80 to 90% by weight of feldspar, 5 to 10% by weight of mica and 5 to 10% by weight of silica； 50 to 60% by weight of waste coal, 30 to 40% by weight of sewage sludge, and 5 to 10% by weight of food waste are mixed to produce an additive. The above additive is mixed with 60 to 70% by weight of the basic material and 30 to 40% by weight of the additive. To prepare a primary mixture, Grinding the primary mixture into 2,000 to 3,000 mesh, The secondary mixture was added to 70 to 80% by weight of the primary mixture, 15 to 25% by weight of the foam auxiliary material, and 3 to 7% by weight of the clam shell, pulverized to 2,000 to 3,000 mesh. Manufacturing process, 20 to 40% by weight of the crushed vinyl or PVC waste to 60 ~ 80% by weight of the secondary mixture at a temperature of 600 ~ 800 ℃ to form a foamed stone containing many pores in the form of hollow artificial artificial reef Process, By using a plurality of pores formed in the artificial reefs of the foamed stone to propagate the sea plant seeds by the process of fixing the artificial reefs breeding the sea plants in the sea water to provide an environment for the habitat of sea life It is.본 발명은 다공성 발포석을 이용한 인공어초의 제조방법에 관한 것으로,장석 80~90중량%와 운모 5~10중량% 및 규석 5~10중량%를 혼합하여 기초물질을 제조하는 과정과,폐석탄 50~60중량%과 하수슬러지 30~40중량% 및 음식물쓰레기 5~10중량%를 혼합하여 부가첨가물을 제조하여 상기의 기초물질 60~70중량%과 부가첨가물 30~40중량%를 혼합하여 1차 혼합물을 제조하는 과정과,상기의 1차 혼합물을 2,000 내지 3,000메시로 분쇄하는 과정과,상기의 1차 혼합물 70~80중량%에 질석을 2,000 내지 3,000메시로 분쇄한 발포보조재 발포보조재 15~25중량%와 2,000 내지 3,000메시로 분쇄한 조개껍질 3~7중량% 첨가하여 2차 혼합물을 제조하는 과정과,상기의 2차 혼합물 60~80중량%에 파쇄한 비닐이나 PVC 폐기물 20~40중량%를 600~800℃의 온도로 발포하여 많은 기공을 포함하는 발포석을 속이 빈 다각형의 인공어초 형태로 형성하는 과정과,상기 발포석의 인공어초에 형성된 다수의 기공을 이용하여 바다식물 씨를 번식하도록 하여 상기 바다식물을 번식시킨 인공어초를 바다물 속에 고정 설치하는 과정으로 구성하여 바다생명체의 서식을 위한 환경을 제공할 수 있도록 한 것이다.