The present invention relates to a method for manufacturing a root canal filler. A method of manufacturing a root canal filler of the present invention comprises a body preparation step of preparing a body comprising a rubber component； A swelling step of bringing the body surface into contact with a solvent to cause the body surface to swell； A coating step of coating a bio-ceramic material on the swelled body； And a drying step of drying the coated body at room temperature for 12 to 36 hours. According to the present invention, the body surface is brought into contact with a solvent so that the trans-1,4-polyisoprene polymer of the body is released in a swelling (swelling) chain, but the polymer chain on the surface side is released by contacting for a short time. After removal of the solvent in a certain amount of time, it is precipitated in the hydroxyapatite powder, which shrinks the polymer chains and crushes the powder particles so that the coating is achieved, which can shorten the production speed as well as the dental root canal with excellent adhesion strength. It becomes possible to manufacture a filler.본 발명은 근관 충전재의 제조 방법에 관한 것이다.본 발명의 근관 충전재의 제조 방법은, 고무 성분을 포함하는 바디를 준비하는 바디준비단계와； 상기 바디 표면을 용매에 접촉시켜 바디 표면이 팽윤 상태가 되도록 하는 팽윤단계와； 상기 팽윤 처리된 바디에 바이오 세라믹 물질을 코팅하는 코팅단계와； 상기 코팅된 바디를 상온에서 12 ~36시간 동안 건조하는 건조단계；를 포함하여 구성된다.본 발명에 의해, 바디 표면을 용매와 접촉시켜 바디의 트랜스-1,4-폴리이소프렌 고분자가 스웰링(팽윤)상태로 사슬이 풀어지도록 하되, 짧은 시간 동안 접촉시켜 표면 측의 고분자 사슬이 풀어질 정도의 시간에 용매를 제거한 후, 하이드록시아파타이트 파우더에 침전하여 고분자 사슬이 수축하면서 파우더 입자를 옭아매어 코팅이 이루어지도록 함으로써 생산 속도를 극 단축시킬 수 있을 뿐만 아니라, 우수한 접착강도를 지닌 치과용 근관 충전재를 제조할 수 있게 된다.