This porous hollow fiber membrane contains polyethersulfone or polysulfone, has an inner diameter of 300 to 600 µm, a thickness of 70 to 200 µm, and a fractional molecular weight of 10,000 or less, comprises a plurality of micropores with a diameter of 0.1 to 0.5 µm on the entire outer surface, and has a swelling ratio of less than 5%. Swelling ratio (%): Each of 20 or more porous hollow fiber membranes is measured for thickness at 10 or more arbitrary sites in a cross section in the width direction, the average thickness is calculated from the thicknesses measured at 200 or more sites in total, and the swelling ratio is calculated on the basis of the formula below. Swelling ratio (%) = (number of sites at which measured thickness is more than 1.3 times larger than average thickness)/(number of thickness measurements) × 100Cette membrane poreuse à fibres creuses contient du polyéthersulfone ou du polysulfone, a un diamètre interne de 300 à 600 µm, une épaisseur de 70 à 200 µm, et un poids moléculaire fractionnel de 10 000 ou moins, comprend une pluralité de micropores ayant un diamètre de 0,1 à 0,5 µm sur toute la surface externe, et a un taux de gonflement inférieur à 5 %. Taux de gonflement (%) : l'épaisseur de chacune de 20 membranes poreuses à fibres creuses ou plus est mesurée à 10 ou plusieurs sites arbitraires dans une section transversale dans la direction de la largeur, l'épaisseur moyenne est calculée à partir des épaisseurs mesurées à 200 sites ou plus au total, et le taux de gonflement est calculé sur la base de la formule ci-dessous. Taux de gonflement (%) = (nombre de sites où l'épaisseur mesurée est plus de 1,3 fois supérieure à l'épaisseur moyenne)/(nombre de mesures d'épaisseur) × 100ポリエーテルスルホン又はポリスルホンを含む中空糸多孔膜であり、内径が３００～６００μｍ、厚さが７０～２００μｍであり、分画分子量が１０,０００以下であり、外表面全体に孔径０.１～０.５μｍの細孔が複数存在し、膨れ率が５％未満である、中空糸多孔膜。 膨れ率（％）：前記中空糸多孔膜２０本以上について、各中空糸多孔膜１本から幅方向の断面の膜厚を任意に１０箇所以上測定し、合計２００箇所以上の膜厚から平均膜厚を算出し、下記式より膨れ率を算出する。 膨れ率（％）＝（平均膜厚の１.３倍を超える膜厚が測定された箇所の数）／（膜厚測定数）×１００