A laminated structure of a base material layer, a barrier layer, and a photocatalyst layer, wherein the barrier layer is an amorphous TiO2 film, and the photocatalyst layer is formed on the surface of the amorphous TiO2 film； and the amorphous TiO2 film Provided is a photocatalytic functional film containing visible light active photocatalytic agent particles. Adding an alcohol solvent and an acid to the titanium precursor to obtain a TiO2 amorphous sol by dehydration and dealcoholization reaction； applying and drying the TiO2 amorphous sol on a substrate to form a barrier layer； and Applying a composition formed by mixing visible light active photocatalyst agent particles to the TiO2 amorphous sol on the barrier layer and drying to form a photocatalyst layer； provide.基材層、バリアー層、及び光触媒層の積層構造であって、前記バリアー層は非結晶性ＴｉＯ２膜で、前記光触媒層は非結晶性ＴｉＯ２膜；及び前記非結晶性ＴｉＯ２膜の表面に形成された可視光活性光触媒剤粒子を含む光触媒機能性フィルムを提供する。チタン前駆体にアルコール溶媒及び酸を加えて脱水及び脱アルコール反応によってＴｉＯ２非結晶性ゾルを得る段階；前記ＴｉＯ２非結晶性ゾルを基材上に塗布及び乾燥してバリアー層を形成する段階；及び前記ＴｉＯ２非結晶性ゾルに可視光活性光触媒剤粒子を混合して形成された組成物を前記バリアー層上に塗布及び乾燥して光触媒層を形成する段階；を含む光触媒機能性フィルムの製造方法を提供する。