The purpose of the present invention is to provide a resin composite that is more wear resistant and has higher fracture energy than conventional resin composites. A resin composite that: is manufactured using 40 to 400 weight parts of inorganic particles, said inorganic particles having been surface-treated by a surface-treatment agent that has a terminal reactive double-bond group or a terminal aromatic group, per 100 weight parts of a resin with a melting point or fluidization point in the 200-500°C range； and has a mean embedding rate, as shown in formula 1, of at least 55%. Also, a method for manufacturing said resin composite and a dental material using same.Formula 1: Mean embedding rate (%) = 100 × [EP/(EP+V)](In formula 1, EP represents the number (count/(10 µm×10 µm)) of exposed inorganic particles in a 10 µm square region of a polished surface of a test piece of the abovementioned resin composite as seen by a scanning electron microscope and V represents the number (count/(10 µm×10 µm)) of holes formed by inorganic particles having come out of the composite in the 10 µm square region in which the EP number was counted.)La présente invention concerne une résine composite qui est plus résistante à l'usure et qui présente une énergie de fracture plus élevée que les résines composites classiques. La résine composite de l'invention est une résine : qui est fabriquée au moyen de 40 à 400 parties en poids de particules inorganiques, lesdites particules inorganiques ayant été traitées en surface par un agent de traitement de surface contenant un groupe réactif terminal à double liaison ou un groupe aromatique terminal, pour 100 parties en poids d'une résine ayant un point de fusion ou un point de fluidisation compris entre 200 °C et 500 °C ； et qui présente un taux moyen d'enrobage, déterminé au moyen de la formule 1, d'au moins 55 %. L'invention concerne également un procédé de fabrication de ladite résine composite et un matériau dentaire l'utilisant.Form