The invention relates to a process for preparing polymer composites with antibacterial properties for drainage tubes, for medical use. According to the invention, the process consists in melt processing, at a temperature of 170°C, for 7 min and a speed of 60 rpm, a mixture comprising 75.6...79.6% polylactic acid, 7.56...7.96% plasticizer, 11.34...11.94% polyethylene glycol, up to 5% collagen hydrolysate, and up to 0.5% silver nanoparticles, the perceintage being expressed by mass, respectively, the resulting mixture is processed at a temperature of 135...150°C, on a screw extruder, provided with a nozzle with a diameter of 4 mm and a mandrel with a diameter of 3 mm, resulting in tubes with an inner diameter of 3 ± 0.1 mm and an outer diameter of 4 ± 0.1 mm, with a resistance to breakage of 16...32 MPa, with a breaking elongation of 126.5...216.8%, stable over short-time and exhibiting antimicrobial and antifungal activity for use as sterile urinary tubes.Invenţia se referă la un procedeu de obţinere a unor compozite polimerice cu proprietăţi antibacteriene, pentru tuburi de drenare, de uz medical. Procedeul conform invenţiei constă în prelucrarea în topitură la o temperatură de 170°C, timp de 7 min, şi o viteză de 60 rpm, a unui amestec format, în procente masice, din 75,6...79,6% acid polilactic, 7,56...7,96% plastifiant, 11,34...11,94% polietilenglicol, până la 5% hidrolizat de colagen, respectiv, până la 0,5% nanoparticule de argint amestecul rezultat se prelucrează pe un extruder cu şnec, la o temperatură de 135...150°C, prevăzut cu o duză cu un diametru de 4 mm şi un dorn cu diametrul de 3 mm, rezultând tuburi cu un diametru interior de 3 ± 0,1 mm, şi un diametru exterior de 4 ± 0,1 mm având o rezistenţă la rupere de 16...32 MPa, o alungire la rupere de 126,5...216,8%, care sunt stabile pe termen scurt, şi prezintă activitate antimicrobiană şi antifungică, pentru utilizare ca tuburi urinare sterile.