The present invention relates to a cremation urn using eco-friendly natural binder and a method of manufacturing the same. A raw material, in which kaolin is mixed with a natural binder at a ratio of kaolin of 80 wt% to 95 wt% and a natural binder of 5 wt% to 20 wt%, is milled with a vacuum pug mill, is molded in a shape of a cremation urn, and then is dried at temperature in the range of 80°；C to 200°；C for a time in the range of 5 hours to 20 hours. Thus, the consumption of energy required for high temperature firing when the cremation urn is manufactured may be reduced and the high strength of the cremation urn may be maintained. In addition, the cremation urn is prevented from being decayed and generating mold, so that the cremation urn is crushed to perfectly become soil when a predetermined time is elapsed after burial.본 발명은 천연 결합제를 사용하는 친환경 수목장용 봉안함 및 그 제조 방법에 관한 것으로, 고령토 80wt.% 이상 95wt.% 이하 및 천연 결합제 5wt.% 이상 20wt.% 이하의 비율로 고령토와 천연 결합제가 혼합된 원료가, 진공 토련기로 토련되고, 봉안함의 형태로 성형되며, 80℃ 이상 200℃ 이하의 온도로 5시간 이상 20시간 이하 동안 건조되어 형성되며, 봉안함의 제조시 고온 소성에 필요한 에너지 소비를 절감할 수 있고, 봉안함이 높은 강도를 유지하고 부패 및 곰팡이의 발생을 방지하며 부패하지 않으면서도 수목장 후 일정 시간이 경과하면 완전히 흙으로 와해될 수 있다.