The invention relates to a layer (20) for protecting the skin and tissues in the vicinity of the skin, comprising a polymer gel obtained by at least partial polymerization of a mixture comprising: about 15% of dimethyl-vinyl-terminated polydimethylsiloxane having a viscosity greater than 20000 mPa.s, about 25% of dimethylvinyl-terminated polydimethylsiloxane having a viscosity of from 200 to 20000 mPa.s, about 45% of trimethyl-terminated polydimethylsiloxane, about 12% of trimethylsiloxy-treated pyrogenic silica, and about 3% of dimethyl-hydrogenated co-polydimethylsiloxane-polymethyl-hydrogenosiloxane, the polymer gel having at 35 ° C, when a biasing frequency varies between 0 and 100 rd / s, a varying stiffness or elastic component. from about 11000 to 20000 Pa, a viscosity or damping component ranging from about 700 to 8000 Pa and a damping factor or Tan Delta varian about 0.06 to 0.38, and forming a protective layer from the polymer gel.L'invention concerne une couche (20) deprotection de la peau et des tissus au voisinage de la peau,comprenant un gel polymère obtenu par polymérisation aumoins partielle d'un mélange comprenant : environ 15%de polydiméthylsiloxane à terminaisons diméthyl-vinylesayant une viscosité supérieure à 20000 mPa.s, environ25% de polydiméthylsiloxaneà terminaisons diméthyl-vinyles ayant une viscosité comprise entre 200 et20000 mPa.s, environ 45% de polydiméthylsiloxane àterminaisons triméthyles, environ 12% de silice de pyrogénation traitéetriméthylsiloxy, et environ 3% deco-polydiméthylsiloxane-polyméthyl-hydrogéno-siloxane à terminaisons diméthyle-hydrogéno, le gel polymère présentant à 35°C,lorsqu'une fréquence de sollicitation varie entre 0 et 100 rd/s, une rigiditéou composante élastique variant d'environ 11000 à20000 Pa, une viscosité ou composante amortissante variant d'environ 700 à8000 Pa et un facteur d'amortissement ou Tan Deltavariant d'environ 0,06 à 0,38, et de formation d'une c