Providing a method of modifying refractory particles used to produce a casting mold by using a furan resin as a binder, so as to effectively improve a strength of the casting mold and to reduce a required amount of the binder. An artificial aggregate which is artificially produced and which has an apparent porosity of not more than 5% is used as the refractory particles, and the artificial aggregate is subjected to a heat treatment at a temperature of 400-1500°C for not shorter than one hour in a heating atmosphere having an oxygen concentration of not higher than 15%.