The invention relates to a process for preparing an oily nanodispersion with tissue regeneration capacity. According to the invention, the process consists in the dispersion, by stirring at 300 rpm, in the matrix support consisting of sunflower oil for injectable use, in a concentration of 2.5...5.0 ppm, of either the colloidal silver with a grain size of 5...10 nm, film-coated with polyvinylpyrrolidone, or some silver nanoparticles obtained from silver nitrate by precipitation with sodium citrate and stabilized in an aqueous system, in the presence of polyvinylpyrrolidone, resulting in a fatty water-in-oil emulsion wherefrom there is obtained the oily nanodispersion of colloidal silver having a particle size of 10 nm, at the most, by applying a vacuum of 0.85 at, at a temperature of 75...80°C, for 20...30 min, the said nanodispersion being packaged as vials to be stored at temperatures of less than 10°C.Invenţia se referă la un procedeu de obţinere a unei nanodispersii uleioase cu capacitate regenerativă a ţesuturilor. Procedeul conform invenţiei constă din dispersarea în suportul matriceal, constând din ulei de floarea soarelui pentru uz injectabil, în concentraţie de 2,5...5,0 ppm, prin agitare cu 300 rot/min, fie a argintului coloidal cu granulaţie de 5...10 nm, peliculizat cu polivinilpirolidonă, fie a unor nanoparticule de argint obţinute din azotat de argint prin precipitare cu citrat de sodiu şi stabilizate în sistem apos, în prezenţa polivinilpirolidonei, rezultând o emulsie grasă de apă în ulei, din care se obţine nanodispersia uleioasă de argint coloidal, cu o dimensiune a particulelor de maximum 10 nm, prin aplicarea unui vid de 0,85 at la o temperatură de 75...80°C, timp de 20...30 min, nanodispersia fiind ambalată în fiole care se păstrează la temperaturi sub 10°C.