A process for fabricating pre-sintered zirconia blanks that are then computer machined and sintered to form dental appliances having highly advantageous features. The principal steps of a preferred embodiment of that process comprise a) preparing a ceramic slurry of binderless zirconia powder b) subjecting the slurry to attrition milling down to about a 5-29 nm crystallite size c) preparing a vacuum assisted and pressure assisted slip casting mold and pouring the milled slurry into the slip-casting mold d) after casting, excess slurry is poured from the mold and a consolidated zirconia blank is removed e) drying the blank and pre-sintering it to form solid blanks ready for CAD/CAM machining and sintering to net shape. The attrition is run with ball bearings that are of the sample material to prevent contamination. It also is run, up to 24 hours, to break down the crystallites to overcome the high density of zirconia.Procédé de fabrication débauches en zircone pré-frittées qui sont ensuite usinées par ordinateur et frittées pour former des appareils dentaires ayant des caractéristiques extrêmement avantageuses. Les principales étapes dun mode de réalisation préféré de ce procédé comprennent a) la préparation dune pâte céramique de poudre de zircone sans liant b) le broyage par frottement de la pâte jusquà une taille de cristallite denviron 5 à 29 nm c) la préparation dun moule de coulage en barbotine sous vide et sous pression et lintroduction de la pâte broyée dans le moule de coulage en barbotine d) après la coulée, la pâte en excès étant versée du moule et une ébauche de zircone consolidée en étant extraite e) le séchage de lébauche et son pré-frittage pour former des ébauches solides prêtes à être usinées par CAO/usinage assisté par ordinateur et le frittage aux cotes du produit fini. Le frottement est réalisé au moyen de roulements à billes qui sont en matériau de léchantillon pour éviter toute contamination. Ce frottement dure jusquà 24 heures, afin de séparer