PURPOSE: A crown manufacturing method is provided to enhance the hardness of a molding product for preventing the crack of the molding product. CONSTITUTION: A crown manufacturing method comprises the following steps. A molding product including the oxide of zirconium is formed so that the molding product is suitable for teeth (S10). The molding product is dried at a temperature of 130°；C-150°；C for 2-3 hours (S11). The dried molding product is colored (S12). The colored molding product is dried for 2 hours (S13). The dried molding product is plasticized for 9-11 hours so that the temperature of the molding product hit a temperature of 15000°；C (S14). The molding product and the teeth are connected (S15). The surface of the molding product becomes shiny (S16). [Reference numerals] (S10) Form a molding product including oxide of zirconium； (S11) Dry the mold product at a temperature of 130°；C-150°；C for 2-3 hours； (S12) Color the dried molding product； (S13) Dry the colored molding product for 2 hours or more； (S14) Plasticize the dried molding product a temperature of 15000°；C or more for 10 hours； (S15) Finish the connection part of the plasticized molding product and the teeth； (S16) Make the surface of the molding product become shiny본 발명은 치아용 크라운 제조방법에 관한 것이다. 본 발명은 지르코늄의 산화물을 포함하는 성형체를 치아의 형상에 맞게 성형하는 성형단계와, 상기 성형체를 130℃ 내지 150℃에서 2시간 내지 3시간동안 건조하는 단계와, 건조된 상기 성형체를 착색하는 단계와, 착색된 상기 성형체를 2시간 이상 건조하는 단계와, 건조된 상기 성형체를 최대온도가 1500℃ 이상이 되도록 9시간 내지 11시간 소성하는 단계와, 소성된 상기 성형체와 치아의 접합부분을 마감하는 단계 및 마감된 상기 성형체의 표면에 광택을 형성하는 단계를 포함한다.이와 같은 본 발명에 의하면 소성단계에서 성형체에 가하는 온도를 상승하는 단계와, 상승된 온도를 1500℃로 유지하는 단계와, 유지된 온도를 하강시키는 단계로 나누어 공정하고, 이때 온도를 상승하는 단계에서 온도가 상승 되는 시간과 온도가 하강하는 단계에서 온도가 하강 되는 시간의 차이는 2배 이상 나도록 하여 성형체가 높은 온도에서 소성되어 서서히 굳어지도록 함에 따라 성형체의 단단함과 견고함을 향상시킴으로써 성형체의 균열을 방지할 수 있다.