The present invention relates to a method for preparing plastic resins for removing odor and volatile organic compounds and, more specifically, to a method for preparing plastic resins for removing odor and volatile organic compounds which comprises: (first step) a step which adds sodium silicate and aluminium silicate to purified water and agitates at 0 to 60 for 1-2 hours； (second step) a step which increases the temperature of the agitated reactant up to 100 to 120°；C while adding calcium nitrate and makes react for 2-5 hours； (third step) a step which obtains powder through filtering and drying after finishing the reaction； and (fourth step) a step which extrudes after mixing the powder with a plastic material. The method for preparing plastic resins for removing odor and volatile organic compounds according to the present invention improves problems of conventional remover powder and effectively reduces polymer material originated odor such as ammonia, amine, aldehyde, and volatile organic compounds and the likes. [Reference numerals] (AA) Stir after adding sodium silicate and aluminium silicate to purified water； (BB) React after adding calcium nitrate to the mixture； (CC) Obtain powder through filtering and drying after finishing reaction； (DD) Manufacture removing agent M/B by extruding after mixing the powder with plastic material； (EE) The first step； (FF) The second step； (GG) The third step； (HH) The fourth step본 발명은 냄새 및 휘발성유기화합물 제거용 플라스틱 수지의 제조방법에 관한 것으로, 보다 상세하게는 정제수에 규산나트륨 및 규산알루미늄을 첨가한 후, 0 내지 60℃에서 1 내지 2 시간 동안 교반시키는 단계(제1단계)； 상기 교반된 반응물을 100 내지 120℃의 온도까지 올리면서 질산칼슘을 첨가한 후, 2 내지 5 시간 동안 반응시키는 단계(제2단계)； 상기 반응이 종결된 후 여과 및 건조를 통해 분말을 수득하는 단계(제3단계)； 및 상기 분말에 플라스틱 소재를 혼합한 후, 압출하는 단계(제4단계)를 포함하는, 냄새 및 휘발성유기화합물(VOC) 제거용 플라스틱 수지의 제조방법을 제공한다.본 발명에 따른 냄새 및 휘발성 유기화합물(VOC) 제거용 플라스틱 수지는 종래 제거제 분말의 문제점을 모두 개선하면서 고분자 소재 유래 냄새 예를 들어, 암모니아, 아민, 알데하이드 및 휘발성 유기화합물 등을 효과적으로 저감시킬 수 있다.