A polyarylene sulfide resin granular article characterized in that the average particle size is from more than 1 μm to 100 μm, the degree of uniformity is 4 or less, the melt viscosity measured at a temperature 300°C and a shear rate of 1216 sec-1 is 150-500 Pa・s, and the recrystallization temperature, defined as the apex temperature of the exothermic peak at the time of crystallization when cooled from 340°C to 50°C at 20°C/min using a differential scanning calorimeter, is 150-210°C. A polyarylene sulfide resin granular article suitable as a material powder for producing a three-dimensional model by a 3D printer with powder sintering can be provided efficiently.