In a molding step, step A1, a base material having a predetermined shape is obtained by molding a polymer material. In a polymer film forming step, step A2, the resulting base material is irradiated with ultraviolet light while immersed in a treatment aqueous solution containing a compound having a phosphorylcholine group and a water-soluble inorganic salt, to form on the surface of the base material a polymer film containing a polymer chain obtained by polymerization of the compound having a phosphorylcholine group. Adopting the method of manufacturing a sliding member for a prosthetic joint as described hereinabove makes it possible to manufacture efficiently a sliding member for a prosthetic joint having excellent wear resistance.Selon linvention, dans une étape de moulage, létape A1, un matériau de base présentant une forme prédéterminée est obtenu par moulage dun matériau polymère. Dans une étape de formation de film polymère, létape A2, le matériau de base obtenu est irradié au moyen dune lumière ultraviolette tout en étant immergé dans une solution aqueuse de traitement contenant un composé présentant un groupe phosphorylcholine et un sel minéral soluble dans leau, en vue de former sur la surface du matériau de base un film polymère contenant une chaîne polymère obtenu par polymérisation du composé présentant un groupe phosphorylcholine. Le procédé de fabrication dun élément coulissant destiné à une articulation prothétique selon linvention permet de fabriquer efficacement un élément coulissant destiné à une articulation prothétique présentant une excellente résistance à lusure.工程A1の成型工程では、高分子材料を成型し、予め定める形状の基材を得る。工程A2の高分子膜形成工程では、得られた基材を、ホスホリルコリン基を有する化合物と水溶性無機塩とを含有する処理水溶液に浸漬させた状態で紫外線を照射し、基材の表面に、ホスホリルコリン基を有する化合物が重合した高分子鎖を含む高分子膜を形成する。以上の人工関節用摺動部材の製造方法により、耐摩耗性に優れた人工関節用摺動部材を効率的に製造することができる。