PROBLEM TO BE SOLVED: To provide a porous implant material having strength characteristics similar to human bone and ensuring adequate bonding with bone even while avoiding the occurrence of a stress shielding phenomenon.SOLUTION: Multiple metal bodies 4, 5 of differing porosities are bonded via bonding interfaces F parallel in one direction, while the porosity of the overall composite of the metal bodies 4, 5 is 50 to 92%. The metal bodies of the higher porosity are porous metal bodies 4 having a three dimensional reticulated structure with multiple communicating pores formed by a continuous bone structure. The metal bodies 5 of the lower porosity has a porosity of 0-50%, and has an area occupancy in cross-sections in a direction orthogonal to the axis direction of 0.5 to 50% when one direction along the bonding interfaces is directed to the axis direction. The strength when compressed in a direction parallel to a direction along the bonding interfaces is 1.4 to 10 times the strength when compressed in a direction along the direction orthogonal to the bonding interfaces.COPYRIGHT: (C)2012,JPO&INPIT【課題】人骨に近い強度特性を有し、ストレスシールディング現象の発生を回避しながらも骨との十分な結合性を確保する。【解決手段】気孔率の異なる複数の金属体4,5が一の方向に平行な接合界面Fを介して接合されるとともに、これら金属体4,5の接合体全体の気孔率が50%~92%であり、気孔率が高い金属体は、連続した骨格により形成される複数の気孔が連通した三次元網目状構造を有する多孔質金属体4であり、気孔率が低い金属体5は、気孔率が0~50%で、かつ接合界面に沿う一の方向を軸心方向としたときに、該軸心方向に直交する方向の断面における面積占有率が0.5%~50%であり、接合界面に沿う方向と平行な方向に圧縮したときの強度は、接合界面に直交する方向と平行な方向に圧縮したときの強度に対して1.4倍~10倍とされている。【選択図】 図2