The present invention relates to a molded body composition for hard tissue regeneration containing magnesium phosphate, a scaffold for hard tissue generation comprising the same, and a method for preparing the same. The scaffold according to the present invention is prepared through a new process of, in order to apply a cement reaction of a magnesium phosphate-based powder having excellent biocompatibility and physical properties to a deposition modeling technology, preparing a three-dimensional molded body of a paste consisting of a magnesium phosphate powder and a thickener and then depositing the molded body in a hardening liquid to induce cementation, leading to the preparation of a scaffold for hard tissue regeneration, thereby securing a sufficient time to control a three-dimensional shape and a pore structure and thus enabling precise structure control, securing sufficient mechanical strength without a high-temperature sintering process, and exhibiting excellent bioactivity and biocompatibility. Therefore, the structural disadvantage of the conventional ceramic scaffold for hard tissue regeneration can be significantly overcome, the basic conditions required for the scaffold can be satisfied, and effects such as the functionalization of the scaffold and the reduction in the manufacturing costs can be expected by simplification of the process simplification and application of the non-heating process.COPYRIGHT KIPO 2014본 발명은 인산마그네슘을 포함하는 경조직 재생용 성형체 조성물, 이를 포함하는 경조직 재생용 지지체 및 이들의 제조방법에 관한 것으로, 본 발명에 따른 지지체는 생체적합성 및 기계적 물성이 우수한 인산 마그네슘계 분말의 시멘트 반응을 적층조형기술에 적용하기 위하여 인산마그네슘 분말과 점증제로 구성된 페이스트로 3차원 성형체를 제조한 후 경화액에 침적시켜 시멘트화를 유도하여 경조직 재생용 지지체를 제조하는 새로운 공정을 통하여 제조되므로 3차원 형상 및 기공구조 제어를 위한 충분한 시간을 확보할 수 있어 면밀한 구조제어가 가능하고 고온 소결공정을 거치지 않고 충분한 기계적 강도를 확보할 수 있으며 생체활성과 생체 적합성이 우수한 것을 특징으로 하고, 따라서 종래의 경조직 재생용 세라믹 지지체의 구조적 단점을 크게 극복하고 지지체에 요구되는 기본 조건을 만족시키며 공정의 단순화와 비가열 공정 적용으로 지지체의 기능화 및 제조비용 절감 등의 효과를 기대할 수 있다.