The present invention relates to a method for manufacturing a sleeve for dental surgical guide, which can actively prevent wear and damage of the sleeve caused by differential surface hardness by using zirconia as a material of the sleeve, not using metals or polymer in the conventional sleeve manufacturing art. More specifically, the sleeve manufacturing method comprises: a raw material mixing step (S10) of mixing 70-80 wt% of zirconia crushed with size of 50-100 μm with 20-30 wt% of a stabilizer made of yttrium trioxide (Y_2O_3)； a molded product generation step (S20) of charging the raw material into a mold with a molding space having an appearance of the sleeve, and pressing the mold； a molded product defatting step (S30) of immerging a molded product into a defatting solution made of 60-70 wt% of a sodium hydroxide maintained at 60-70°C and 30-40 wt% of a natural surfactant； a molded product sintering step (S40) of sintering the molded product in an elevation type electric furnace at 45-50 °C/min of heating rate and 1,400-1,500°C of the temperature for 0.5-1 hour； and a molded product post-processing step (S50) of performing a heat treatment operation at 1,100-1,400°C for 1-20 hours four or five times after processing the appearance of the molded product.본 발명은 기존의 메탈 혹은 폴리머로 슬리브를 제조하던 방식에서 벗어나 지르코니아 소재로 슬리브를 제조함으로써 차별되는 표면 경도로 인한 슬리브의 마모 및 파손을 적극적으로 예방할 수 있는 치과용 써지컬 가이드를 위한 슬리브 제조방법에 관한 것으로, 더욱 상세하게는 50~100㎛의 크기로 분쇄한 지르코니아 70~80 중량%와, 삼산화이트륨(Y₂O₃)으로 구성된 안정제 20~30 중량%로 배합하는 원료 배합단계(S10)；와, 원료를 슬리브 외형의 성형공간을 갖춘 금형에 장입한 뒤 가압하는 성형품 생성단계(S20)；와, 60 내지 70℃의 온도로 유지되는 수산화나트륨 용액 60~70 중량%와, 천연 계면활성제 30~40중량%로 구성된 탈지용액에 성형품을 침지하는 성형품 탈지단계(S30)；와, 승강식 전기로에서 승온속도 45~50℃/min로 1,400~1,500℃에서 30분~1시간 동안 소결하는 성형품 소결단계(S40)；와, 성형품의 외형을 가공한 뒤, 1,100~1,400℃에서 1~20시간 동안 4~5회 열처리하는 성형품 후처리 단계(S50)；를 순차 거쳐 이루어진다.