PROBLEM TO BE SOLVED: To provide a dental adhesive composition that satisfies three of high bond strength, fracture energy (toughness) and a long operation time.SOLUTION: The dental adhesive resin cement comprises (A) 100 parts by mass of a (meth)acrylate-based polymerizable monomer, (B) 40-200 parts by mass of a polymethyl methacrylate powder mixture composed of (b1) 35-92 mass% of a substantially noncrosslinked polymethyl methacrylate powder having a weight-average molecular weight of 100,000-1,200,000 and a specific surface area of 0.1-0.6 (m2/g), (b2) 4-45 mass% of a substantially noncrosslinked polymethyl methacrylate powder having a weight-average molecular weight of 100,000-600,000 and a specific surface area of 0.7-5 (m2/g) and (b3) 4-25 mass% of a substantially noncrosslinked polymethyl methacrylate powder having a weight-average molecular weight of 1,000-80,000 and (C) an effective amount of a polymerization initiator and is separately packed at least in a liquid material containing the component (A) and a powder material containing the component (B).COPYRIGHT: (C)2009,JPO&INPIT【課題】高い接着強度と破断エネルギー(靭性)、および長い操作時間の3者を両立可能な歯科用接着性組成物を開発する。【解決手段】(A)(メタ)アクリレート系重合性単量体 100質量部、(B)下記組成b1)重量平均分子量が10万~120万であり、比表面積が0.1~0.6(m2/g)である実質的に非架橋のポリメチルメタクリレート粉末35~92質量%,b2)重量平均分子量が10万~60万であり、比表面積が0.7~5(m2/g)の実質的に非架橋のポリメチルメタクリレート粉末4~45質量%,b3)重量平均分子量が1千~8万である実質的に非架橋のポリメチルメタクリレート粉末4~25質量%からなるポリメチルメタクリレート粉末混合物 40~200質量部(C)有効量の重合開始剤を含んでなり、少なくとも(A)成分を含む液材と(B)成分を含む粉材とに分包されてなる歯科用接着性レジンセメントとする。【選択図】 なし