A process for the production of rounded zinc peroxide particles with an average particle diameter of 0.04 µm or more and an aspect ratio of 2.0 or less, comprising a step (1) of adding an aqueous solution of hydrogen peroxide at a concentration of 1 to 500 g / l in terms of hydrogen peroxide to a suspension of zinc oxide particles as raw material at a concentration of 10 to 2000 g / l in terms of zinc oxide, and stir the mixture, the amount of hydrogen peroxide treatment is 0.7 times or more of the number of moles relative to zinc oxide as raw material, in which the average particle diameter of rounded zinc peroxide particles it is measured as described in paragraph [0015] of the description, and the aspect ratio of the zinc peroxide particles is measured as described in paragraph [0018] of the description.Un procedimiento para la producción de partículas redondeadas de peróxido de zinc con un diámetro promedio de partícula de 0,04 μm o más y una relación de aspecto de 2,0 o menos, que comprende una etapa (1) de añadir una solución acuosa de peróxido de hidrógeno a una concentración de 1 a 500 g/l en términos de peróxido de hidrógeno a una suspensión de partículas de óxido de zinc como materia prima a una concentración de 10 a 2000 g/l en términos de óxido de zinc, y agitar la mezcla, la cantidad de tratamiento de peróxido de hidrógeno es de 0,7 veces o más del número de moles en relación con el óxido de zinc como materia prima, en el que el diámetro promedio de partícula de las partículas redondeadas de peróxido de zinc se mide como se describe en el párrafo [0015] de la descripción, y la relación de aspecto de las partículas de peróxido de zinc se mide como se describe en el párrafo [0018] de la descripción.