Provided are medical supplies which have excellent antimicrobial activity and are superior in the durability of antimicrobial activity and in biocompatibility and to a method of producing the medical supplies. A base material is treated by carrying out anodic oxidation treatment to perform electrolysis by applying pulsed current having a frequency of 50 to 10000 Hz to the base material in an acid electrolytic bath or alkali electrolytic bath, to form a film having micro pores and/or micro unevennesses having a density of preferably 5 × 10 4 /mm 2 on the surface of the base material and then, by carrying out iodine-impregnation treatment to impregnate the film with iodine or iodine compounds. The iodine compound is preferably polyvinyl pyrrolidone iodine, ²-cyclodextrin iodine or silver iodide. Further, the base material is preferably a metallic material and any one of Ti or Ti alloy, stainless steel, and a Co-Cr alloy having biocompatibility. The film may be formed by using any one of medicine treatment, thermal processing treatment and mechanical processing treatment or a combination of these treatments in place of the anodic oxidation treatment. This produces such an effect that medical supplies which have excellent antimicrobial activity and are superior in the durability of antimicrobial activity and in biocompatibility can be produced easily at low costs.항균성이 우수하고 항균성의 지속성이 높고, 또한 생체친화성이 높은 의료용 부품 및 그 제조 방법을 제공한다. 기재에, 산성 전해욕 또는 알칼리성 전해욕 내에서 주파수 50~10000㎐의 펄스상 전류를 인가하고 전해 처리를 행하는 양극 산화를 실시하여 상기 기재 표면에 바람직하게는 5×104개/㎟ 이상의 미세 구멍 및 미세 요철 중 하나 이상을 가지는 피막을 형성한 후에, 상기 피막에 요오드 또는 요오드 화합물을 함침시키는 요오드 함침 처리를 행한다. 또한, 요오드 화합물은 폴리비닐필로리돈 요오드, β-시클로덱스트린 아이오다인 및 요오드화은 중 어느 하나로 하는 것이 바람직하다. 또한, 기재는 금속재료이고, 생체친화성을 가지는 Ti, Ti 합금, 스테인레스강 및 Co-Cr 합금 중 어느 하나로 하는 것이 바람직하다. 또한, 양극 산화 처리를 대신하여 약품 처리, 열가공 처리 및 기계가공 처리 중 어느 하나 혹은 이것들의 조합 등으로 피막을 형성할 수 있다. 이에 따라 우수한 항균성, 우수한 항균성의 지속성을 가지고, 생체친화성도 높은 의료용 부품을 용이하고 값싸게 제조할 수 있다는 효과가 있다.